10+4Composite wear-resistant steel plate10+5/10+6/10+8/10+10

Click on the picture to see the original picture
brand: Wan Rong
Hrc: 62
Unit Price: 1.00yuan/kg
Start up: 1 kg
Total supply volume: 777777 kg
period for dispatch: From the date of the buyer's payment 3 Delivery within days
Location: Tianjin
Valid until: Long term effectiveness
Last update: 2019-04-04 14:35
Browse times: 1533
purchase
Basic company information
 
 
Product Details
10+4Composite wear-resistant steel plate10+5/10+6/10+8/10+10Surfacing manufacturer

 Advantages of wear-resistant composite steel plate: specifications (m)
Substrate (mm)
Actual thickness (mm)
Total thickness (mm)
Hardness (HRC)
C content (%)
Cr content (%)
4+4 
1.47x3.41
4.5 
3.5-4 
8-8.5 
57-62 
3.0-4.5 
20-30 
5+5 
6, coal processing industry - feed trough, hopper, crusher parts and liners, coal pipelines, elbows, scraper conveyor floor, pump body.
Specification
Available in size (m)
Substrate (mm)
Actual thickening (mm)
Total thickness (mm)
Hardness (HRC)
C content (%)
Cr content (%) 
4+4 
1.4*3.0 
4.5 
3.5-4 
8-8.5 
57-62 
3.0-4.5 
20-30 
5+5 
1.4*3.0 
5.5 
4.5-5 
10-10.5 
57-62 
3.5-5.0 
25-35 
6+5 
1.4*3.0 
7.5 
3.5-4 
11-11.5 
57-62 
3.5-5.0 
25-35 
6+6 
1.4*3.0或1.4*3.5 
7.5 
4.5-5 
12-12.5 
58-63 
3.5-5.0 
27-37 
8+5 
1.4*3.0 or 1.4*3.5 10+4 composite wear-resistant steel plate 10+5/10+6/10+8/10+10 surfacing manufacturer
9.5 
3.5-4 
13-13.5 
57-62 
3.5-5.0 
25-35 
8+6 
1.4*3.0 or 1.4*3.5 
9.5 
4.5-5 
14-14.5 
58-63 
3.5-5.0 
27-37 
8+8 
1.4*3.0 or 1.4*3.5 
9.5 
6.5-7 
16-16.5 
60-65 
3.5-5.0 
28-38 
10+5 
1.4*3.0 or 1.4*3.5 or 2.1*3.5 
11.5 
3.5-4 
15-15.5 
57-62 
3.0-4.5 
20-30 
10+6 
Ibid 
11.5 
4.5-5 
16-16.5 
58-63 
3.5-5.0 
27-37 
10+7 
Ibid 
11.5 
5.5-6 
17-17.5 
58-63 
3.5-5.0 
27-37 
10+8 
Ibid 
11.5 
6.5-7 
18-18.5 
60-65 
3.5-5.0 
28-38 
10+10 
Ibid 
11.5 
8.5-9 
20-20.5 
60-65 
4.0-5.5 
30-40 
The specifications we provide are 12+5, 12+6, 12+7, 12+8, 12+10, 12+1, 12+1, 14+6, 14+8, 14+10, 16+6, 16 +8, 16+10, 18+6, 18+8, 18+10, 20+6, 20+8, 20+10, 30+10, 40+10, etc., can also be customized
 

10+4 composite wear-resistant steel plate 10+5/10+6/10+8/10+10 surfacing manufacturer 1. Super wear resistance performance ratio: wear test shows that the wear resistance of chromium carbide surfacing and wear-resistant composite steel plate is higher than ordinary The steel plate is 10-30 times higher than the cast stainless steel and high manganese steel, and is twice as high as the as-cast high-chromium iron, which is roughly equal to the ceramic magnet. HRC≤63
2, high impact resistance ratio: Because the base metal is made of Q235A soft steel substrate, the surface is made of chromium carbide multi-element hardfacing surfacing composite superhard material. It fully embodies the dual advantages of composite materials with both super wear resistance and impact toughness. This is beyond the reach of as-cast wear resistant materials. (Traditional castings have poor impact resistance and are brittle and easy to break)
3, convenient processing performance ratio: maintenance workers can arbitrarily according to the field size cutting (plasma cutting), it is very convenient to wear the wear-resistant steel plate on the surface of the wear parts (carbon steel surface), can also be processed into counterbore The bolt is attached to the component. It can also be bent into the inner cold, such as: wear-resistant pipes, dust-removing elbows, various shaped round-shaped places and other plate members. (The wear-resistant plates of castings cannot be assembled by welding methods. It is also difficult to cast large-area wear-resistant plates for cast steel. In addition, traditional castings are cumbersome, because they are designed to prevent deformation.)
4, high performance and low cost ratio: the use of wear-resistant surfacing composite steel plate, although the cost is increased, the price is about 3-5 times higher than the ordinary steel plate, 25% cheaper than the high chromium stainless steel casting. However, considering the service life of the machine, reducing the maintenance cost, the loss of labor and other human and financial losses, etc., due to the rational use of materials, its performance brings multiple gains to production.
Plate size: 1500x6000mm (can also be made according to user requirements)
Wear-resistant layer alloy composition: C: 5.0%, Cr: 27-30%, martensite matrix + a large number of Cr7C3 type carbides of more than 60%
Composite wear-resistant steel plate hardness: alloy layer macro hardness HRC57-65, carbide hardness HV1400-1800
Abrasion resistance: 20-25 times of low carbon steel, 8-12 times of stainless steel and high manganese steel, 1.5 times or more of general high carbon high chromium wear resistant steel plate
High temperature resistance: normal type <600 ° C; high temperature type <1000 ° C
Impact resistance: The wear-resistant alloy layer is completely metallurgically bonded to the substrate, resisting strong impact, and does not have to worry about falling off.
Industry application range:
        Steel industry: hopper lining, distributor chute, fan blade wear lining, dust elbow pipe, hammer lining, four-roller roll, single-roll crushing spindle, slab surfacing repair, slag chute, Cloth disc, vibrating feeder lining, vibrating screen lining, mineral material hopper, bucket cutter blade, slag conveying wear parts.
       Power industry: fan blades, burner lines, feed troughs and hopper liners, crusher components, coal mill components, ash pipes, air handling systems and conveyors.
       Cement industry: surfacing repair of vertical grinding rolls and grinding discs, impact discs, pipes, pump casings, mill linings, crusher parts, slag tapping tanks, various chassis, vibrating screen linings.
       Paper industry: cyclone lining, screw conveyor, feed trough and funnel, fan blades, conversion ducts, transition elbows.
       Mining industry: truck cargo tank lining, hopper lining, feed trough lining, crusher components, cover plates, wear-resistant rod wear plates.
       Coal processing industry: feed trough, hopper, crusher parts and liners, coal pipelines, elbows, pump bodies.
        Product introduction: Chromium carbide high-hard wear-resisting surfacing steel plate is a metal arc generated by the submerged arc (arc) arc and the surface of the base metal plate. The special alloy powder and the welding wire are synchronously adjusted and plated by a professional process. In the molten pool, the wear-resistant alloy material is automatically welded.
        QG wear-resistant steel plate adopts a special processing technology. The carbide in the surface metallographic structure is fibrous, and the fiber direction is perpendicular to the surface layer. The wear-resistant alloy layer is cracked and designed to eliminate stress, which does not affect the normal wear-resistant steel plate. For use, the surface hardness can reach up to HRC62, and secondary hardening will occur in a certain temperature range.
        The alloy layer of XT wear-resistant steel plate is mainly composed of chromium carbide, and is also equipped with molybdenum, niobium, titanium, boron and other components. The formation of multi-element carbides also has strong stability at high temperatures, and can still be kept below 500°. High hardness and good oxidation resistance. The mother board adopts Q235A soft base steel plate with good toughness. The new composite steel plate with two materials combines wear resistance, corrosion resistance, temperature resistance and impact resistance. This is unachievable for casting high manganese and high chromium stainless steel. It is the most ideal new material to replace traditional castings.
 
More» Other products of our company

[ Device search ]  [ Join in collection ]  [ Tell your friends ]  [ Print this article ]  [ Illegal reporting ]  [ close window ]

Website Homepage

About Us

Contact

Use Agreement

Copyright privacy

Sitemap

Service Items

Member Service

Advertising Services

Website Message

Four Privileges

Payment Method

Apple APP Download
Android App Download
Mining Club
Contact Us

029-85212477

We are always waiting for your visit!

| ICP business license: Shaanxi ICP No. 15507745